Semiconductor devices including a diode structure over a conductive strap and methods of forming such semiconductor devices

ABSTRACT

Semiconductor devices including at least one diode over a conductive strap. The semiconductor device may include at least one conductive strap over an insulator material, at least one diode comprising a single crystalline silicon material over a conductive material, and a memory cell on the at least one diode. The at least one diode may be formed from a single crystalline silicon material. Methods of forming such semiconductor devices are also disclosed.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is related to co-pending U.S. patent application Ser. No. 12/715,704 filed on Mar. 2, 2010, and titled “SEMICONDUCTOR-METAL-ON-INSULATOR STRUCTURES, METHODS OF FORMING SUCH STRUCTURES, AND SEMICONDUCTOR DEVICES INCLUDING SUCH STRUCTURES”; co-pending U.S. patent application Ser. No. 12/715,843 filed on Mar. 2, 2010, and titled “FLOATING BODY CELL STRUCTURES, DEVICES INCLUDING SAME AND METHODS FOR FORMING SAME; co-pending U.S. patent application Ser. No. 12/715,889 filed on Mar. 2, 2010, and titled “THYRISTOR-BASED MEMORY CELLS, DEVICES AND SYSTEMS INCLUDING THE SAME AND METHODS FOR FORMING THE SAME”; and co-pending U.S. patent application Ser. No. 12/715,922 filed on Mar. 2, 2010, and titled “SEMICONDUCTOR CELLS, ARRAYS, DEVICES AND SYSTEMS HAVING A BURIED CONDUCTIVE LINE AND METHODS FOR FORMING SAME”, the disclosures of which are incorporated herein by reference.

TECHNICAL FIELD

The present invention, in various embodiments, relates generally to semiconductor structures including a diode and methods of forming such semiconductor structures. More specifically, embodiments of the present invention relate to a diode structure having a conductive strap, devices including such a diode structure, and methods of forming such a diode structure.

BACKGROUND

One of the common trends in the electronics industry is the miniaturization of electronic devices. This is especially true for electronic devices operated through the use of semiconductor microchips. Microchips are commonly viewed as the so-called “brains” of most electronic devices. In general, a microchip comprises a small silicon wafer upon which are built thousands of microscopic electronic devices that are integrally configured to form electronic circuits. The circuits are interconnected in a unique way to perform a desired function.

With the desire to decrease the size of electronic devices, it is also necessary to decrease the size of the microchip and electronic devices thereon. This movement has increased the number and complexity of circuits on a single microchip.

Conventionally, electronic devices are formed side-by-side in a single plane on a common substrate, such as a silicon wafer. This side-by-side positioning, however, uses a relatively large amount of surface area or so-called “real estate” on the substrate. As a result, larger substrates are required.

A recent trend is to vertically stack semiconductor devices on a single substrate. However, the stacking of semiconductor devices adds an additional degree of complexity to arranging the components of the semiconductor device. Furthermore, the processing conditions for fabrication of stacked or superimposed devices must be controlled so as not to damage components in underlying devices. In addition to stacking semiconductor devices, individual devices may be formed having high aspect ratios (i.e., the ratio of height to width). However, these high aspect ratios can increase the risk of the breakage of the device because of the limited surface area of the bond between the device to the substrate. Similarly, as the size of the devices decrease, interconnects, such as bit lines and word lines, may also need to decrease in size, e.g., width. In some cases, the size of the device may be so small that it becomes impractical, if not impossible, to form interconnects of the desired size on the device.

One common type of electronic device found on a microchip is a diode. A diode functions as a type of electrical gate or switch. An ideal diode will allow an electrical current to flow through the diode in one direction but will not allow the electrical current to flow through the diode in the opposite direction. In conventional diodes, however, a small amount of current flows in the opposite direction. This is referred to as current leakage.

Conventional diodes are typically formed from a silicon material that is modified through a doping process. Doping is a process in which ions are diffused or implanted within the silicon and then activated. There are two general types of dopants: P-type dopants and N-type dopants. P-type dopants produce positive charged holes. In contrast, N-type dopants produce extra electrons with negative charges. In general, a semiconductor diode is formed when a material doped with a P-type dopant is placed adjacent to a material with an N-type dopant.

Conventionally, diodes are configured by positioning the two opposing doped materials side-by-side on a microchip. This side-by-side positioning, however, uses a relatively large amount of surface area on a microchip. As a result, larger microchips are required.

Furthermore, for a diode to operate, each side of the diode must have an electrical connection that either brings electricity to or from the diode. The minimal size of each side of the diode is in part limited in that each side must be large enough to accommodate an electrical connection. Since conventional diodes have a side-by-side configuration with each side requiring a separate electrical connection, the ability to miniaturize such diodes is limited. In addition, the requirement of having side-by-side electrical connections on a single diode increases the size and complexity of the microchip.

In order to rectify some of these shortcomings, various attempts have been made to form a vertical diode structure. For example, U.S. patent application Ser. No. 12/434,212 (now U.S. Pat. No. 8,034,716) to Gonzalez et al. titled Method of Making Semiconductor Structures Including Vertical Diode Structures, hereinafter referred to as “Gonzalez” and the disclosure of which is incorporated herein in its entirety by reference, describes one method of making a vertical diode structure. However, such vertical diode structures are formed using a polysilicon material which has a poor I_(or)/I_(off) performance due to the low carrier mobility through the polysilicon material. Current leaks may also form at a grain boundary of the polysilicon material, thus also decreasing the I_(on)/I_(off) performance of the diode. The method of forming such vertical diodes, as described in Gonzalez, also does not provide an adequate means of forming an electrical contact for the diode when the diode is miniaturized, such as when the width of the diode is less than about 20 nm.

Accordingly, there is a need for a method of forming a vertical semiconductor device including a diode which provides high I_(on)/I_(off) performance and provides for easy accessibility of an electrical contact, such as a conductive strap, to the diode. Additionally, there is a need for a method of forming such diodes as part of a semiconductor device wherein the diode may be formed over a first electronic device without damaging the first electronic device.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-8 are partial perspective views of a semiconductor device including a diode and a conductive strap during various processing acts in accordance with one embodiment of the disclosure;

FIGS. 9-14 are partial perspective views of a semiconductor device including a diode and a conductive strap during various processing acts in accordance with one embodiment of the disclosure; and

FIG. 15 is a schematic block diagram illustrating one embodiment of an electronic system that includes a semiconductor device including a diode and a conductive strap of the disclosure.

DETAILED DESCRIPTION

A diode structure over a conductive strap, devices including such structures, and methods of forming such a structure are disclosed. The diode structure includes, for example, a conductive strap formed over an insulator material and a diode formed of a single crystalline silicon material formed over the conductive strap. The diode may be a vertical diode structure having a first doped region formed over the conductive strap and a second doped region formed over the first doped region. A memory cell may be formed over the diode. Methods of forming such structures include forming a base structure including a second semiconductor substrate having a first doped region and a second doped region, a conductive material, an adhesion material, and an insulator material over a first semiconductor substrate. A portion of the second semiconductor substrate, the conductive material, and the adhesion material may be removed to form the conductive strap and the diode structure.

The diode structures formed in accordance with the various embodiments of the disclosure are formed of a single crystalline silicon material. In contrast, conventional diodes are formed of a polysilicon material. Such conventional diodes exhibit poor I_(on)/I_(off) performance due to the low carrier mobility in the polysilicon material and current leaks, which typically form at the boundaries of the silicon grains. By forming the diode from a single crystalline silicon material, the I_(on)/I_(off) performance of the diode may be improved as the single crystalline silicon material has greater ion mobility than polysilicon material. In addition, current leaks are less likely to form within the single crystalline silicon material. Additionally, because single crystalline silicon material is stronger than polysilicon material, the diodes formed from the single crystalline silicon material may be smaller than a diode formed of polysilicon material.

The methods for forming the diode structures in accordance with various embodiments of the disclosure include forming a second semiconductor substrate overlying a conductive material. Because the conductive material, which may be used to form a conductive strap, is buried beneath the second semiconductor substrate, the diode structure may be formed in the second semiconductor substrate in relatively few process acts, as described in greater detail below. For example, in one embodiment, a cross point array including a plurality of diodes having a memory cell formed on each diode may be formed in as few as two patterning and etching acts. Furthermore, because the diode structures are formed over the conductive strap, the diode structures may be self-aligned with the conductive strap and, thus, contact resistance caused by misalignment between the diode and the conductive strap may be reduced. The memory cell and the diode may also be self aligned, thus decreasing contact resistance caused by misalignment between the diode and the memory cell.

The diode structures formed in accordance with various embodiments of the disclosure may be used to fabricate a variety of semiconductor devices, such as an integrated circuit including a logic device formed in/on the first semiconductor substrate and a memory device including the diode structure formed in/on the second semiconductor substrate. Since a logic device may be formed on the first semiconductor substrate before the memory device including the diode structure is formed, the memory device is not exposed to the processing conditions used for the formation of the logic device. By forming such vertical integrated circuits, the cell size may be reduced, which provides for increased cache memory density. The diode structures formed in accordance with various embodiments of the disclosure may be used to form, for example, flash memory, imagers, and phase change memory (PCRAM).

The following description provides specific details, such as material types and processing conditions, in order to provide a thorough description of embodiments of the present invention. However, a person of ordinary skill in the art will understand that the embodiments of the present invention may be practiced without employing these specific details and in conjunction with conventional fabrication techniques. In addition, the description provided herein does not form a complete process flow for manufacturing a semiconductor device including the diode structure. Only those process acts and structures necessary to understand the embodiments of the present invention are described in detail below. Additional acts to form a complete semiconductor device including the diode structure according to an embodiment of the invention may be performed by conventional techniques.

The materials described herein may be formed by any suitable technique including, but not limited to, spin coating, blanket coating, chemical vapor deposition (“CVD”), plasma enhanced chemical vapor deposition (“PECVD”), atomic layer deposition (“ALD”), plasma enhanced ALD, or physical vapor deposition (“PVD”). Alternatively, materials may be grown in situ. A technique suitable for depositing or growing a particular material may be selected by a person of ordinary skill in the art. While the materials described and illustrated herein may be formed as layers, the materials are not limited thereto and may be formed in other three-dimensional configurations.

In the following detailed description, reference is made to the accompanying drawings, which form a part hereof, and in which is shown, by way of illustration, specific embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable a person of ordinary skill in the art to practice the invention. However, other embodiments may be utilized, and structural, logical, and electrical changes may be made without departing from the scope of the invention. The illustrations presented herein are not meant to be actual views of any particular system, logic device, memory cell, or semiconductor device, but are merely idealized representations which are employed to describe the present invention. The drawings presented herein are not necessarily drawn to scale. Additionally, elements common between drawings may retain the same numerical designation.

Referring now to the drawings, where like elements are designated by like reference numerals, FIGS. 1 through 8 are partial perspective views of a method of forming an embodiment of a semiconductor device 100 (FIG. 8) of the present invention. The semiconductor device 100 (FIG. 8) may be formed using a semiconductor structure 34 (FIG. 4), also referred to herein as a base structure 34, which is formed by bonding an acceptor wafer 10 (FIG. 1) and a donor wafer 16 (FIG. 2). Forming such base structures 34 are described in detail in U.S. patent application Ser. No. 12/715,704 filed on Mar. 2, 2010, and titled “SEMICONDUCTOR-METAL-ON-INSULATOR STRUCTURES, METHODS OF FORMING SUCH STRUCTURES, AND SEMICONDUCTOR DEVICES INCLUDING SUCH STRUCTURES”. While FIGS. 1 through 4 illustrate one example of a method of forming the base structure 34, any of the methods described in U.S. patent application Ser. No. 12/715,704, or other known methods, may be utilized to form the base structure 34.

FIG. 1 depicts the acceptor wafer 10. The acceptor wafer 10 may include a first semiconductor substrate 12 having an insulator material 14 formed thereon. The first semiconductor substrate 12 may include a fabrication substrate, such as a full or partial wafer of semiconductor material (e.g., silicon, gallium arsenide, indium phosphide, etc.), a full or partial silicon-on-insulator (SOI) type substrate, such as a silicon-on-glass (SOG), silicon-on-ceramic (SOC), or silicon-on-sapphire (SOS) substrate, or any other known, suitable fabrication substrate. As used herein, the term “wafer” includes conventional wafers as well as other bulk semiconductor substrates. The first semiconductor substrate 12 may be doped or undoped. An at least partially fabricated logic device (not shown), such as a CMOS (complementary metal-oxide semiconductor) device, may optionally be present on the first semiconductor substrate 12 and may be formed by conventional techniques. In one embodiment, the first semiconductor substrate 12 is bulk crystalline silicon.

The insulator material 14 may be a dielectric material including, by way of non-limiting example, silicon dioxide, borophosphosilicate glass (BPSG), borosilicate glass (BSG), phosphosilicate glass (PSG), or the like. In one embodiment, the insulator material 14 is an oxide. The insulator material 14 may be from about 500 Å thick to about 2 μm thick, such as from about 1000 Å to about 2000 Å. Techniques for deposition and in situ growth of such dielectric materials are known in the art and may include, for example, chemical vapor deposition (CVD), such as low pressure CVD or plasma enhanced CVD, atomic layer deposition (ALD), spin-on deposition, thermal decomposition, or thermal growth.

FIG. 2 is a partial perspective view of one embodiment of the donor wafer 16 used to form the base structure 34 (FIG. 4). The donor wafer 16 may include a precursor semiconductor substrate 18 formed of a single crystalline silicon material. A conductive material 20 and an adhesion material 22 may be formed over the precursor semiconductor substrate 18. The precursor semiconductor substrate 18 may, initially, be doped or undoped. By way of example, the precursor semiconductor substrate 18 may initially be a single crystalline silicon material that is undoped or intrinsically doped. The precursor semiconductor substrate 18 may then be doped, or further doped, to include a first doped region 24, a second doped region 26, and a lightly doped region 28. These doped regions may ultimately form the diode. The first doped region 24 and the second doped region 26 may be doped with P-type or N-type dopants such that the first doped region 24 and the second doped region 26 are oppositely doped. For example, in one embodiment, the first doped region 24 is an N-type single crystalline silicon material and the second doped region 26 is a P-type single crystalline silicon material. Alternatively, in another embodiment, the first doped region 24 is a P-type single crystalline silicon material and the second doped region 26 is an N-type single crystalline silicon material. A lightly doped region 28 may be formed between the first doped region 24 and the second doped region 26. The lightly doped region 28 may be doped with the same dopant as the second doped region 26, but the lightly doped region 28 may have a lower concentration of dopant than the second doped region 26. For example, the second doped region 26 may be doped with a higher concentration of the P-type dopant and the lightly doped region 28 may be doped with a lower concentration of the P-type dopant. If the first doped region 24 is an N-type single crystalline silicon material, a Schottky diode may be formed at an interface between the first doped region 24 and the conductive material 20, as known in the art. While the doped regions 24, 26, and 28 are described as being formed before the donor wafer 16 and acceptor wafer 10 are bonded, doping of the precursor semiconductor substrate 18 to form these regions may be conducted after the donor wafer 16 and the acceptor wafer 10 are bonded.

The doped regions 24, 26, and 28 may be formed by a doping technique known in the art, such as diffusion or ion implantation techniques. By way of example, if the first doped region 24 is an N-type single crystalline silicon material, the first doped region 24 may be formed by implanting ions of an N-type impurity, such as arsenic (As), phosphorous (P) or antimony (Sb), into the precursor semiconductor substrate 18. If the second doped region 26 is a P-type single crystalline silicon material, the second doped region 26 may be formed by implanting ions of a P-type impurity, such as boron (B), into the precursor semiconductor substrate 18. As known in the art, the depth to which the ions are implanted into the precursor semiconductor substrate 18 is at least partially a function of the implant dose and energy. The depth of the implanted ions within the precursor semiconductor substrate 18 may correspond to a desired thickness of the first doped region 24 and the second doped region 26. The first doped region 24 and the second doped region 26 may be formed before or after the conductive material 20 and the adhesion material 22 have been formed on the donor wafer 16. The lightly doped region 28 may be doped using the same dopant as the second doped region 26, except that a lower concentration of the dopant is implanted, such as by adjusting the implant dose or implant energy.

The conductive material 20 may be a low resistivity conductive material including, but not limited to, a phase change material, titanium, titanium silicide, titanium oxide, titanium nitride, tantalum, tantalum silicide, tantalum oxide, tantalum nitride, tungsten, tungsten silicide, tungsten oxide, tungsten nitride, other metals, metal silicide, metal oxide, or metal nitride materials, or combinations thereof, including multiple, different conductive materials. In one embodiment, the conductive material 20 is formed from titanium nitride because titanium nitride has good adherence or adhesion to many materials, such as the single crystalline silicon material used as the precursor semiconductor substrate 18. Titanium nitride also has a high melting point (about 3000° C.), which makes it unaffected by high processing temperatures. Titanium nitride also makes excellent ohmic contact with other conductive materials. Titanium nitride is also commonly used in semiconductor fabrication and, therefore, may easily be incorporated into conventional fabrication processes. In one embodiment, the conductive material 20 is a titanium-rich titanium nitride, such as metal mode titanium nitride (MMTiN). The conductive material 20 may also be formed from multiple conductive materials. By way of non-limiting example, the conductive material 20 may be formed from a metal, such as titanium, tungsten or aluminum, with a layer of titanium material formed thereon. The thickness of the conductive material 20 may be optimized, depending on the material, to provide a low ohmic contact. For example, if the conductive material 20 is titanium nitride, such as MMTiN, the conductive material 20 may have a thickness of from about 10 nm to about 50 nm. The conductive material 20 may be formed by a deposition technique known in the art, such as, for example, ALD, CVD, or PVD.

The adhesion material 22 may include, for example, an amorphous material, such as an amorphous silicon material or an amorphous germanium material. The adhesion material 22 may be formed over the conductive material 20 by a deposition technique known in the art, such as, for example, ALD, CVD, or PVD. In one embodiment, the adhesion material 22 may be formed on the conductive material 20 by PVD, followed by chemical-mechanical planarization (CMP). The adhesion material 22 may be of sufficient thickness to adhere to the insulator material 14 of the acceptor wafer 10 as described in greater detail below. For example, the thickness of the adhesion material 22 may be from about 10 nm to about 50 nm.

The donor wafer 16 may also include a cleave portion 30 formed by implanting an atomic species into the precursor semiconductor substrate 18. The atomic species may be hydrogen ions, ions of rare gases, also termed inert or noble gases, or ions of fluorine. The atomic species may be implanted into the precursor semiconductor substrate 18 of the donor wafer 16 to form an implanted zone 32. The atomic species may be implanted into the precursor semiconductor substrate 18 prior to formation of the conductive material 20 thereon, after formation of the conductive material 20 thereon, or after formation of the adhesion material 22 thereon. The implanted zone 32 may be formed at a desired depth in the precursor semiconductor substrate 18, which is dependent on parameters such as implant dose and energy of the atomic species, as known in the art. The location of the implanted zone 32 may correspond to a height of a diode 48 ultimately formed from the precursor semiconductor substrate 18, as shown in FIG. 7. The implanted zone 32 may include microbubbles or microcavities including the implanted atomic species, which provide a weakened region within the precursor semiconductor substrate 18. The donor wafer 16 may be thermally treated at a temperature above that at which implantation is effected, but below the melting temperature of the conductive material 20, to effect crystalline rearrangement in the donor wafer 16 and coalescence of the microbubbles or microcavities. As described below, the donor wafer 16 may be cleaved at the implanted zone 32, forming the second semiconductor substrate 18′ on the base structure 34 (FIG. 4) and cleave portion 30. For convenience and clarity, the term “second semiconductor substrate” is used herein to refer to the semiconductor structure after removal of the cleave portion 30, while the term “precursor semiconductor substrate” is used herein to refer to the semiconductor structure before removal of the cleave portion 30.

As shown in FIG. 3, the donor wafer 16 (FIG. 2) may be superposed onto the acceptor wafer 10 (FIG. 1) such that the adhesion material 22 of the donor wafer 16 is in contact with the insulator material 14 of the acceptor wafer 10. The adhesion material 22 of the donor wafer 16 may then be bonded to the insulator material 14 of the acceptor wafer 10 by exposure to heat. Prior to bonding the donor wafer 16 to the acceptor wafer 10, at least one of the adhesion material 22 and the insulator material 14 may, optionally, be treated to improve the bond strength between the adhesion material 22 and the insulator material 14. Such treatment techniques are known in the art and may include chemical, plasma, or implant activations. For example, the insulator material 14 may be treated with a dilute ammonia hydroxide or hydrogen fluoride solution. The adhesion material 22 may also be exposed to a plasma of, for example, argon, to form a plasma-activated surface. Activating at least one of the adhesion material 22 and the insulator material 14 may increase the kinetics of the subsequent bonding therebetween

As shown in FIG. 3, the adhesion material 22 of the donor wafer 16 may be contacted and bonded with the insulator material 14 of the acceptor wafer 10 to form a precursor of the base structure 34 (FIG. 4). The adhesion material 22 may be bonded to the insulator material 14 by, for example, heating the base structure 34 to a temperature of less than about 600° C., such as from about 300° C. to about 400° C. If the insulator material 14 is formed from silicon dioxide, silicon-oxide bonds may form between the adhesion material 22 and the insulator material 14. Because the conductive material 20 may be formed of a metal or other heat sensitive material, the temperature to which the base structure 34 is exposed may be less than the melting point of the conductive material 20. The adhesion material 22 and the insulator material 14 may also be bonded without heat, such as at ambient temperature (from about 20° C. to about 25° C.). Pressure may also be applied to the donor wafer 16 and the acceptor wafer 10 to bond the adhesion material 22 to the insulator material 14. Once the donor wafer 16 is bonded to the acceptor wafer 10, the conductive material 20 from the donor wafer 16 may form a buried conductive material, which is disposed between the insulator material 14 and the precursor semiconductor substrate 18.

The cleave portion 30 may then be removed from the precursor semiconductor substrate 18 to form the base structure 34 shown in FIG. 4. The cleave portion 30 may be removed by techniques known in the art, such as by applying a shear force to the implanted zone 32 or by applying heat or a jet gas stream at the implanted zone 32. The hydrogen or other ions implanted in implanted zone 32 produce a weakened region in the precursor semiconductor substrate 18, which is susceptible to cleavage. The remaining portion of the precursor semiconductor substrate 18 (second semiconductor substrate 18′) may have a thickness, for example, of from about 50 nm to about 500 nm (from about 500 Å to about 5000 Å). The second semiconductor substrate 18′ of the base structure 34 may be smoothed according to conventional techniques such as, for example, one or more of grinding, wet etching, and chemical-mechanical planarization (CMP).

The base structure 34 may be formed by modification of SMART-CUT® layer transfer technology. The SMART-CUT® layer transfer technology is described in detail in, for example, U.S. Pat. No. RE 39,484 to Bruel, U.S. Pat. No. 6,303,468 to Aspar et al., U.S. Pat. No. 6,335,258 to Aspar et al., U.S. Pat. No. 6,756,286 to Moriceau et al., U.S. Pat. No. 6,809,044 to Aspar et al., U.S. Pat. No. 6,946,365 to Aspar et al., and U.S. Patent Application Publication No. 2006/0099776 to DuPont. However, other processes suitable for manufacturing a semiconductor substrate having a buried conductive material may also be used, if sufficiently low process temperatures are maintained. In conventional implementation of the SMART-CUT® layer transfer technology, donor wafers and acceptor wafers are bonded together using a high temperature anneal. The temperature used to bond the donor and acceptor wafers is from about 1000° C. to about 1300° C. However, due to the presence of the conductive material 20 in the semiconductor structures described herein, the semiconductor structures of the present invention may, in some embodiments, be unable to withstand exposure to such temperatures without thermal damage. Accordingly, as described above, lower temperatures may be used to bond an acceptor wafer 10 and donor wafer 16.

As shown in FIG. 5, a bottom electrode 36, a memory medium 38, and a top electrode 40 may be formed over the second semiconductor substrate 18′. If the second semiconductor substrate 18′ were not previously doped, as described above, the second semiconductor substrate 18′ may be doped prior to forming the bottom electrode 36, the memory medium 38, and the top electrode 40. The bottom electrode 36 may be formed from a conductive material, such as titanium, titanium silicide, titanium nitride, tungsten, tungsten silicide, tungsten nitride, or combinations thereof. In one embodiment, the bottom electrode 36 is MMTi, titanium, MMTi/titanium nitride, or titanium/titanium nitride. The bottom electrode 36 may be formed over the second semiconductor substrate 18′ using a deposition technique known in the art, such as, for example, ALD, CVD, or PVD. The memory medium 38 may be formed of any medium capable of holding distinct detectable states. By way of non-limiting example, the memory medium 38 may be formed of a transition metal material, such as nickel oxide or copper oxide, a phase change material, such as a chalcogenide material, or a resistive oxide material. For example, the memory medium 38 may be formed of a chalcogenide material having the formula Ge_(x)Sb_(y)Te_(z) wherein the ratio of x:y:z=2:2:5, commonly referred to as GST. Additional examples of the memory medium 38 include a conductive oxide material, a solid electrolyte material, an antifuse oxide material, an ovonic material, or a ferroelectric material. The memory medium 38 may also be formed by a deposition technique known in the art, such as, ALD, CVD, or PVD. The top electrode 40 may be formed of a conductive material similar to the bottom electrode 36.

As shown in FIGS. 6 and 7, a two mask process may be used to define a cross point array including at least one diode 48 having a memory cell 46 thereon formed over a conductive strap 42. Referring to FIG. 6, the top electrode 40, the memory medium 38, the bottom electrode 36, the second semiconductor substrate 18′, the conductive material 20, and the adhesion 22 material may be patterned using a single mask to form pillars 45 having at least one first trench 44 there between. As shown in FIG. 6, the top electrode 40, the memory medium 38, the bottom electrode 36, the second semiconductor substrate 18′, the conductive material 20, and the adhesion material 22 may be patterned and etched in a first direction Y, as described in greater detail below. The conductive material 20 underlying the pillars 45 forms the conductive strap 42, which may also function as a word line in the semiconductor device 100 (FIG. 8).

The pillars 45 may be formed by depositing a mask material (not shown) over the top electrode 40 and patterning the mask material to form apertures through which surfaces of the top electrode 40 are exposed. The mask material may include, for example, a photoresist material, an oxide material, transparent carbon, or amorphous carbon. Methods of forming and patterning the mask material are known in the art and, therefore, are not described in detail herein. The pattern in the mask material may then be transferred to the underlying materials using dry or wet etch techniques. By way of non-limiting example, an anisotropic reactive ion (i.e., plasma) etching or reactive ion etching (RIE) process may be used. The etch technique may be selected by a person of ordinary skill in the art based on the material to be removed. Multiple materials may also be removed simultaneously, depending on the similarity in materials. The techniques for removing the underlying materials are conventional and, therefore, are not described in detail herein. The removed portions of the top electrode 40, the memory medium 38, the bottom electrode 36, the second semiconductor substrate 18′, the conductive material 20, and the adhesion material 22 may form the at least one first trench 44. The portions of each of the top electrode 40, the memory medium 38, the bottom electrode 36, the second semiconductor substrate 18′, the conductive material 20, and the adhesion material 22 remaining under the mask material form the pillars 45. The conductive material 20 at the bottom of the pillars 45 forms the conductive strap 42. A portion of the insulator material 14 may also be etched in order to ensure complete electrical isolation of adjacent conductive straps 42 from one another. The remaining portions of the mask material overlying the pillars 45 may then be removed. By way of non-limiting example, the at least one first trench 44 may be formed extending in a first direction Y through each of the top electrode 40, the memory medium 38, the bottom electrode 36, the second semiconductor substrate 18′, the conductive material 20, and the adhesion material 22. For example, if the top electrode 40, the bottom electrode 36, and the conductive material 20 are each formed from titanium nitride, a mixture of bromine-containing gas and a fluorine-containing gas or a mixture of a fluorine-containing gas and a chlorine-containing gas may be used to remove each of these titanium nitride materials and the adhesion material 22 selective to the mask material and the insulator material 14. The second semiconductor substrate 18′ may be selectively removed using a reactive ion etching (RIE) process using oxygen (O₂) gas and tetrafluoromethane (CF₄) gas. A fill material (not shown) may be formed in the at least one first trench 44 and subject to CMP so that an upper surface 43 of the base structure 34 is substantially planar. The fill material may include, for example, a dielectric material such as an oxide material, a nitride material, or a spin-on-glass (SOG) material, and may be deposited using a chemical vapor deposition process.

As shown in FIG. 7, portions of the top electrode 40, the memory medium 38, the bottom electrode 36, and the second semiconductor substrate 18′ may be patterned using a second mask to form at least one diode 48 having a memory cell 46 formed thereon. The diode 48 includes the first doped region 24, the lightly doped region 28, and the second doped region 26. The memory cell 46 includes the bottom electrode 36, the memory medium 38, and the top electrode 40. At least one second trench 47 may be formed between adjacent diodes 48 over a common conductive strap 42. To form the diodes 48, the top electrode 40, the memory medium 38, the bottom electrode 36, and the second semiconductor substrate 18′ including the second doped region 26, the lightly doped region 28 and a portion of the first doped region 24 may be patterned and etched in a second direction X to form at least one second trench 47, as described in greater detail below. The second direction X may be substantially perpendicular to the first direction Y. As shown in FIG. 7, the diode 48 is self-aligned with the conductive strap 42 thus eliminating the need for a separate electrical contact between the diode 48 and the conductive strap 42. Similarly, the memory cell 46 is self-aligned with the diode 48, which eliminates the need for a separate electrical contact between the memory cell 46 and the diode 48. The aspect ratio of each diode 48 may be from about 2:1 to about 20:1 and, more particularly, from about 5:1 to about 10:1. The width of each diode 48 may be from about 5 nm to about 50 nm and, more particularly, from about 10 nm to about 20 nm. Because the diode 48 is formed of a single crystalline silicon material rather than a polysilicon material, the diode 48 may have a smaller width and height than a diode formed of polysilicon material.

Conventional diodes formed of a polysilicon material have a lower carrier mobility than and experience a greater occurrence of leaks along the grain boundary, thus providing a lower performance than a diode formed of a single crystal silicon material. Additionally, because the diode 48 is formed of a single crystalline silicon material, the diode 48 may have a greater ability to transfer ions than a diode formed from polysilicon and, therefore, will have a greater I_(on)/I_(off) performance than a polysilicon diode.

Each diode 48 and memory cell 46 may be formed by depositing a mask material (not shown) over the top electrode 40 and the fill material (not shown) and patterning the mask material to form apertures through which surfaces of the top electrode 40 are exposed. Optionally, surfaces of the fill material (not shown) may also be exposed through the mask material. The mask material may include, for example, a photoresist material, an oxide material, transparent carbon or amorphous carbon. Methods of forming and patterning the mask material are known in the art and, therefore, are not described in detail herein. Portions of the top electrode 40, the memory medium 38, the bottom electrode 36, and the second semiconductor substrate 18′ including the second doped region 26, the partially doped region 28, and a portion of the first doped region 24 that are exposed through the apertures in the mask material may be removed to form each diode 48 and memory cell 46. For example, if the top electrode 40 and the bottom electrode 26 are each formed from titanium nitride, a mixture of bromine-containing gas and a fluorine-containing gas or a mixture of a fluorine-containing gas and a chlorine-containing gas may be used to remove each of the titanium nitride materials selective to the mask material and the insulator material 14. The second semiconductor substrate 18′ may be selectively removed using a reactive ion etching (RIE) process using oxygen (O₂) gas and tetrafluoromethane (CF₄) gas. An additional fill material (not shown) may be formed in any etched portions of the at least one first trench 44 and the at least one second trench 47 and subject to CMP so that the upper surface 43 of the base structure 34 and the fill material are substantially planar with one another.

As shown in FIG. 8, at least one bit line 50 may be formed over the top electrode 40 of the memory cell 46. In one embodiment, the at least one bit line 50 may electrically couple more than one of the memory cell 46. For example, the bit line 50 may extend in the second direction X over adjacent memory cells 46, electrically coupling memory cells 46 on at least two distinct conductive straps 42. The bit line 50 may be formed by depositing a conductive material over the semiconductor base 34 (FIG. 7) and patterning the conductive material to form substantially straight and substantially parallel bit lines 50. The bit line 50 may patterned and etched, as known in the art, in the second direction X to expose the at least one second trench 47.

The resulting semiconductor device 100 shown in FIG. 8 includes a cross-point diode memory array including the first semiconductor substrate 12, the insulator material 14, the adhesion material 22 bonded to the insulator material 14, the conductive material 20 over the adhesion material 22, wherein the conductive material 20 and the adhesion material 22 form at least two conductive straps 42, a plurality of diodes 48 formed over the at least two conductive straps 42, a memory cell 46 formed on each of the plurality of diodes 48, and a bit line 50 formed over the memory cells 46.

FIGS. 9-14 illustrate another method of forming a semiconductor device 200 (FIG. 14) of the present invention. FIG. 9 illustrates a base structure 34, which is a substantial duplication of FIG. 4 and may be formed as described above regarding FIGS. 1-4. As shown in FIG. 9, the base structure 34 includes a first semiconductor substrate 12, an insulator material 14, an adhesion material 22, a conductive material 20, and a second semiconductor substrate 18′ including a first doped region 24, a lightly doped region 28, and a second doped region 26.

As shown in FIG. 10, a bottom electrode 52 may be formed over the second semiconductor substrate 18′. If the second semiconductor substrate 18′ was not previously doped, as described above, the second semiconductor substrate 18′ may be doped prior to forming the bottom electrode 52. The bottom electrode 52 may be formed from a conductive material, such as titanium, titanium silicide, titanium nitride, tungsten, tungsten silicide, tungsten nitride, or combinations thereof. In one embodiment, the bottom electrode 52 is MMTi, titanium, MMTi/titanium nitride, or titanium/titanium nitride. The bottom electrode 52 may be formed on the second semiconductor substrate 18′ using a deposition technique known in the art, such as, for example, ALD, CVD, or PVD.

As shown in FIGS. 11 and 12, a two mask process may be used to define a cross point array including at least one diode 62 having a bottom electrode 52 thereon formed over a conductive strap 54. Referring to FIG. 11, the bottom electrode 52, the second semiconductor substrate 18′, the conductive material 20, and the adhesion material 22 may be removed using a first mask to form pillars 58 having trenches 56 there between. To form the pillars 58, the bottom electrode 52, the second semiconductor substrate 18′, the conductive material 20, and the adhesion material 22 may be patterned and etched in a first direction Y as described in greater detail below. The conductive material 20 underlying the pillars 58 forms the conductive strap 54, which may also function as a word line in the semiconductor device 200 (FIG. 14).

The pillars 58 may be formed by depositing a mask material (not shown) over the bottom electrode 52 and patterning the mask material to form apertures through which surfaces of the bottom electrode 52 are exposed. The mask material may include, for example, a photoresist material, an oxide material, transparent carbon or amorphous carbon. Methods of forming and patterning the mask material are known in the art and, therefore, are not described in detail herein. The pattern in the mask material may then be transferred to the underlying materials using dry or wet etch techniques. By way of non-limiting example, an anisotropic reactive ion (i.e., plasma) etching or reactive ion etching (RIE) process may be used. The etch technique may be selected by a person of ordinary skill in the art based on the material to be removed. Multiple materials may also be removed simultaneously, depending on the similarity in materials. The techniques for removing the underlying materials are conventional and, therefore, are not described in detail herein. The removed portions of the bottom electrode 52, the second semiconductor substrate 18′, the conductive material 20, and the adhesion material 22 may form the trenches 56. The portions of each of the bottom electrode 52, the second semiconductor substrate 18′, the conductive material 20, and the adhesion material 22 remaining under the mask material form the pillars 58. The conductive material 20 at the bottom of the pillars 58 forms the conductive strap 54. A portion of the insulator material 14 may also be etched in order to ensure complete electrical isolation of adjacent conductive straps 54 from one another. The remaining portions of the mask material overlying the pillars 58 may then be removed. By way of non-limiting example, the trenches 56 may be formed extending in a first direction Y through each of the bottom electrode 52, the second semiconductor substrate 18′, the conductive material 20, and the adhesion material 22. For example, if the bottom electrode 52 and the conductive material 20 are each formed from titanium nitride, a mixture of bromine-containing gas and a fluorine-containing gas or a mixture of a fluorine-containing gas and a chlorine-containing gas may be used to selectively remove each of these titanium nitride materials and the adhesion material 22 selective to the mask material and the insulator material 14. The second semiconductor substrate 18′ may be selectively removed using a reactive ion etching (RIE) process using oxygen (O₂) gas and tetrafluoromethane (CF₄) plasma. A fill material (not shown) may be formed in the trenches 56 and subject to CMP so than an upper surface 60 of the semiconductor base 34 is substantially planar. The fill material may include, for example, a dielectric material such as an oxide material, a nitride material, or a spin-on-glass (SOG) material, and may be deposited using a chemical vapor deposition process.

As shown in FIG. 12, portions of the bottom electrode 52 and the second semiconductor substrate 18′ may be removed using a second mask to form at least one diode 62 having the bottom electrode 52 formed thereon. A trench 64 may be formed between adjacent diodes 62 over a common conductive strap 54. To form the diodes 62, the bottom electrode 52 and the second semiconductor substrate 18′ including the second doped region 26, the lightly doped region 28 and a portion of the first doped region 24 may be patterned and etched in a second direction X to form the trench 64 as described in greater detail below. The second direction X may be substantially perpendicular to the first direction Y. As shown in FIG. 12, the diode 62 is self aligned with the conductive strap 54, thus eliminating the need for a separate electrical contact between the diode 62 and the conductive strap 54. The aspect ratio of each diode 62 may be from about 5:1 to about 40:1 and, more particularly, from about 20:1 to about 30:1. The width of each diode 62 may be about 5 nm to about 40 nm and, more particularly, from about 10 nm to about 20 nm. Because the diode 62 is formed of a single crystalline silicon material rather than a polysilicon material, the diode 62 may have a smaller width and height than a diode formed of polysilicon material. Additionally, because the diode 62 is formed of a single crystalline silicon material, the diode 62 may have a greater ability to transfer ions than a diode formed from polysilicon, and, therefore, will have a greater I_(on)/I_(off) performance than a polysilicon diode.

Each diode 62 may be formed by depositing a mask material (not shown) over the bottom electrode 52 and the fill material (not shown) and patterning the mask material to form apertures through which surfaces of the bottom electrode 52 are exposed. Optionally, surfaces of the fill material (not shown) may also be exposed through the mask material. The mask material may include, for example, a photoresist material, an oxide material, transparent carbon or amorphous carbon. Methods of forming and patterning the mask material are known in the art and, therefore, are not described in detail herein. Portions of the bottom electrode 52 and the second semiconductor substrate 18′ including the second doped region 26, the partially doped region 28, and a portion of the first doped region 24 that are exposed through the apertures in the mask material may be removed to form each diode 62 having the bottom electrode 52 formed thereon. For example, if the bottom electrode 52 is formed from titanium nitride, a mixture of bromine-containing gas and a fluorine-containing gas or a mixture of a fluorine-containing gas and a chlorine-containing gas may be used to selectively remove the titanium nitride materials selective to the mask material and the insulator material 14. The second semiconductor substrate 18′ may be selectively removed using a reactive ion etching (RIE) process using oxygen (O₂) gas and tetrafluoromethane (CF₄) gas. An additional fill material (not shown) may be formed in any etched portions of the trenches 56 and the trenches 64 and subject to CMP so that the upper surface 60 of the semiconductor structure and the fill material are substantially planar with one another.

As shown in FIG. 13, a memory medium 66 may be formed over the bottom electrode 52. The memory medium 66 may be formed of any medium known in the art capable of holding a distinct detectable state or holding a charge. In one embodiment, the memory medium 66 may be formed of a phase change or resistant material such as a chalcogenide material. For example, the memory medium 66 may be formed of a chalcogenide material having the formula Ge_(x)Sb_(y)Te_(z) wherein the ratio of x:y:z=2:2:5, commonly referred to as GST. Additional examples of the memory medium 66 include a conductive oxide material, a solid electrolyte material, an antifuse oxide material, an ovonic material, and a ferroelectric material. The memory medium 66 may be formed by a deposition technique known in the art, such as, for example ALD, CVD, or PVD. In one embodiment, the memory medium 66 may be blanket deposited over the upper surface 60 (FIGS. 11 and 12) of the semiconductor structure. The memory medium 66 may then be patterned and etched as known in the art and as previously described herein such that the memory medium 66 is formed over each of the bottom electrodes 52.

As shown in FIG. 14, at least one bit line 68 may be formed over the memory medium 66. The bit line 68 may act as both a bit line and a top electrode. The bottom electrode 52, the memory medium 66, and the bit line 68 may form a memory cell 70. The at least one bit line 68 may electrically couple more than one memory cell 70. For example, the bit line 68 may extend in the second direction X over adjacent memory cells 70, electrically coupling memory cells 70 on two distinct conductive straps 54. The bit line 68 may be formed by depositing a conductive material over the base structure 34 and patterning the conductive material to form substantially straight and substantially parallel bit lines 68. In one embodiment, a fill material (not shown) may be deposited in the trenches 56 and the trenches 64 as previously described and the bit line 68 may be blanket deposited over the pillars 58 and the fill material. The bit line 68 may then be patterned and etched, as known in the art, in the second direction X to expose the trenches 64.

The resulting semiconductor device 200 shown in FIG. 14 includes a cross-point diode memory array including the first semiconductor substrate 12, the insulator material 14, the adhesion material 22 bonded to the insulator material 14, the conductive material 20 over the adhesion material 22, wherein the conductive material 20 and the adhesion material 22 form at least two conductive straps 54, a plurality of diodes 62 formed over the at least two conductive straps 54, memory cells 70 formed on each of the plurality of diodes 62, wherein the top electrode of the memory cell 70 is the bit line 68. The semiconductor device 200 formed according to FIGS. 9-14 may be substantially similar to the semiconductor device 100 formed according to FIGS. 1-8 with the exception that in the semiconductor device 200, the bit line 68 is the top electrode of the memory cell 70 while in the semiconductor device 100, the bit line 50 is electrically coupled to the top electrode 40 of the memory cell 46.

Semiconductor devices like those previously described herein may be used in embodiments of electronic systems of the present invention. For example, FIG. 15 is a block diagram of an illustrative electronic system 300 according to the present invention. The electronic system 300 may include, for example, a computer or computer hardware component, a server or other networking hardware component, a cellular telephone, a digital camera, a personal digital assistant (PDA), portable media (e.g., music) player, etc. The electronic system 300 includes at least one memory device 301. The electronic system 300 may further include at least one electronic signal processor device 302 (often referred to as a “microprocessor”). At least one of the electronic signal processor device 302 and the at least one memory device 301 may include, for example, an embodiment of the semiconductor device 100, 200 described above. In other words, at least one of the electronic signal processor device 302 and the at least one memory device 301 may include an embodiment of a semiconductor device including a diode structure over a conductive material as previously described in relation to the semiconductor devices 100, 200 shown in FIGS. 8 and 14, respectively. The electronic system 300 may further include one or more input devices 304 for inputting information into the electronic system 300 by a user, such as, for example, a mouse or other pointing device, a keyboard, a touchpad, a button, or a control panel. The electronic system 300 may further include one or more output devices 306 for outputting information (e.g., visual or audio output) to a user such as, for example, a monitor, a display, a printer, an audio output jack, a speaker, etc. In some embodiments, the input device 304 and the output device 306 may include a single touchscreen device that can be used both to input information to the electronic system 300 and to output visual information to a user. The one or more input devices 304 and output devices 306 may communicate electrically with at least one of the memory device 301 and the electronic signal processor device 302.

CONCLUSION

In some embodiments, the present invention includes semiconductor devices including diode structures having a conductive strap and methods for forming such devices. Such devices may include a conductive material over an insulator material, at least one diode comprising a single crystalline silicon material over the conductive material, the diode having a first doped region overlying the conductive material and a second doped region overlying the first doped region wherein the conductivity of the first doped region is opposite the conductivity of the second doped region, and a memory cell over the second doped region. The memory cell may include a bottom electrode, a memory medium, and a top electrode. In some embodiments, the top electrode may be a bit line. In other embodiments, a bit line may be electrically coupled to the memory cell.

In additional embodiments, the present invention includes a semiconductor device that includes an insulator material on a first semiconductor substrate, an adhesion material bonded to the insulator material, a conductive material over the adhesion material, wherein the conductive material and the adhesion material are patterned to form at least one conductive strap, at least one diode over the conductive strap, and a memory cell on the at least one diode. The conductive strap may comprise a word line.

In additional embodiments, the present invention includes a semiconductor device including a first semiconductor substrate having an insulator material thereon, an adhesion material bonded to the insulator material, a conductive material over the adhesion material, wherein the conductive material and the adhesion material are patterned to form at least two conductive straps, a plurality of diodes on each of the at least two conductive straps, each diode comprising a single crystalline silicon material, and a plurality of memory cells, one memory cell of the plurality of memory cells being on each of the plurality of diodes.

In yet further embodiments, the present invention includes methods for fabricating a semiconductor device that include forming a base comprising a second semiconductor substrate comprising a single crystalline silicon material having a first doped region and a second doped region, a conductive material, an adhesion material, and an insulator material overlying a first semiconductor substrate, forming a top electrode, a memory medium, and a bottom electrode over the second semiconductor substrate, removing a portion of the top electrode, the memory medium, the bottom electrode, the second semiconductor substrate, the conductive material, and the adhesion material to form at least one conductive strap having a pillar of the top electrode, the memory medium, the bottom electrode and the second semiconductor substrate thereon, and removing another portion of the top electrode, the memory medium, the bottom electrode, and the second semiconductor substrate to form at least one diode over the at least one conductive strap having a memory cell on the at least one diode.

In yet further embodiments, the present invention includes methods of forming a semiconductor device that include forming a base comprising a second semiconductor substrate comprising a single crystalline silicon material having a first doped region and a second doped region, a conductive material, an adhesion material, and an insulator material overlying a first semiconductor substrate, forming a bottom electrode over the second semiconductor substrate, removing a portion of the bottom electrode, the second semiconductor substrate, the conductive material, and the adhesion material to form at least one conductive strap having a pillar of the bottom electrode and the second semiconductor substrate thereon, and removing another portion of the bottom electrode, and the second semiconductor substrate to form at least one diode over the at least one conductive strap having a portion of the bottom electrode on the at least one diode, forming a memory medium over each portion of the bottom electrode, and forming at bit line over the memory medium.

While the invention is susceptible to various modifications and alternative forms, specific embodiments have been shown by way of example in the drawings and have been described in detail herein. However, the invention is not intended to be limited to the particular forms disclosed. Rather, the invention is to cover all modifications, equivalents, and alternatives falling within the scope of the invention as defined by the following appended claims and their legal equivalents. 

What is claimed is:
 1. A semiconductor device, comprising: a first semiconductor substrate; a second semiconductor substrate over and bonded to the first semiconductor substrate; a conductive material of the second semiconductor substrate being over an insulator material comprised by the first semiconductor substrate in a bonded structure, the bonded structure having an amorphous adhesive material between and contacting the insulator material and the conductive material, the amorphous adhesive material comprising one or both of amorphous silicon and amorphous germanium, the amorphous adhesive material and the conductive material being patterned; at least one diode comprising a single crystalline silicon material over the conductive material, the at least one diode comprising a first doped region overlying the conductive material and a second doped region overlying the first doped region, wherein a conductivity of the first doped region is opposite a conductivity of the second doped region; and a memory cell over the second doped region; the memory cell comprising a bottom electrode, a memory medium, and a top electrode; the top electrode being a bit line in contact with the memory medium without electrically coupling to any separate top electrode material between the bit line and the memory medium.
 2. The semiconductor device of claim 1, wherein the first doped region comprises an N-type doped region and the second doped region comprises a P-type doped region.
 3. The semiconductor device of claim 1, wherein the first doped region comprises a P-type doped region and the second doped region comprises an N-type doped region.
 4. The semiconductor device of claim 1, wherein the at least one diode has a width of less than about 20 nm.
 5. The semiconductor device of claim 1, wherein the at least one diode has an aspect ratio of less than about 20:1.
 6. A semiconductor device, comprising: a first semiconductor substrate comprising an insulative material over a semiconductive material; a second semiconductor substrate over and bonded to the first semiconductor substrate, the second substrate having a conductive material and an adhesive material over the conductive material, the adhesive material comprising one or both of amorphous silicon and amorphous germanium, being distinct from the insulative material and being over and contacting the insulative material of the first substrate in the bonded structure, the second substrate being patterned such that trenches extend through all materials comprised by the second substrate, a base surface of each trench being an upper surface of the insulative material comprised by the first substrate; at least one diode comprising a single crystalline silicon material over the conductive material in the bonded structure, the at least one diode comprising a first doped region overlying the conductive material and a second doped region overlying the first doped region, wherein a conductivity of the first doped region is opposite a conductivity of the second doped region; and a memory cell over the second doped region.
 7. The semiconductor device of claim 6, wherein the adhesion material comprises amorphous silicon.
 8. The semiconductor device of claim 6, wherein the adhesion material comprises amorphous germanium.
 9. A semiconductor device comprising: an insulator material on a first semiconductor substrate; a word line structure adhered to the insulator material, the word line structure comprising a patterned amorphous adhesion material comprising one or both of amorphous silicon and amorphous germanium contacting the insulator material, and conductive material contacting the adhesion material, the conductive material being on a second substrate, the first and second substrates being bonded to one another by the adhesion material; at least one diode on the conductive material, the adhesion material and the conductive material forming a longitudinally coextensive strap portion extending laterally beyond each of opposing lateral edges of the diode; and a memory cell on the at least one diode.
 10. The semiconductor device of claim 9, further comprising a logic device formed on the first semiconductor substrate.
 11. The semiconductor device of claim 9, wherein the at least one diode comprises a single crystalline silicon material.
 12. The semiconductor device of claim 9, wherein the adhesion material comprises amorphous silicon.
 13. The semiconductor device of claim 9, wherein the adhesion material comprises amorphous germanium.
 14. A semiconductor device, comprising: a first semiconductor substrate; a second semiconductor substrate over and bonded to the first semiconductor substrate; a conductive material comprised by the second substrate over an insulator material comprised by the first substrate; a distinct amorphous adhesive material between and being in direct contact with each of the conductive material and the insulative material, the amorphous adhesive material comprising one or both of amorphous silicon and amorphous germanium, the amorphous adhesive material and the conductive material being commonly patterned; at least one diode comprising a single crystalline silicon material over the conductive material, the at least one diode comprising: a first doped region overlying the conductive material and a second doped region overlying the first doped region, wherein a conductivity type of the first doped region is opposite a conductivity type of the second doped region; and a third doped region between the first and second doped regions, the third doped region being of conductivity type the same as one of the first and second doped regions but of lower dopant concentration than said one of the first and second doped regions; and a memory cell over the second doped region. 